Styrene Butadiene Rubber
Styrene Butadiene Rubber
SBR 1500 1502 1712
Packing:Packaging: 35KG/bag with inner PE film
Good Quality ,reasonable price !
Styrene Butadiene Rubber
Styrene Butadiene Rubber (SBR) 1500 /1502/1712
Our production lines goes through a series of processes such as free radical initiated emulsion polymerization, admixture(or oil charge) and coagulation reprocessing, adopting low temperature emulsion polymerization process and redox-catalyst system and using butadiene and styrene as the major raw materials.
The Three types of SBR 1500/1502/1712 were widely used in tyres, cycle tire, rubber overshoes, plastic hosoe tapes, conveyors, rubber tubes, black sole, rubber lines, rice polishing rollers, extruded products, medical products and other colorful or light- colored rubber products.
Compared with natural rubbers, it has excellent wear resistance, natural aging resistance, ozone resistance, water proof property, air tightness and homogeneity, and can be mixed with natural rubber at any ratio.
SBR 1502 Specification Values(GB/T12824-2002)
Item
Property
Test Method
A
B
C
Volatile matter %
≤0.60
≤0.75
≤0.90
GB/T 6737-1997
Ash %
≤0.50
GB/T 4498-1997 A
Organic acid %
4.50-6.75
GB/T 8657-2000 A
Soap %
≤0.50
Bound styrene %
22.5-24.5
GB/T 8658-1998
Mooney viscosity 50ML(1+4)100
45-55
44-56
GB/T 1232.1-2000
Compound 50ML(1+4)100
≤93
300%
145MPa,
300%Modulus
25min
M±2.0
M±2.5
GB/T 8656-1998 A
35min
20.6±2.0
20.6±2.5
50min
21.5±2.0
21.5±2.5
Tensile strength (145,35min), MPa
≥25.5
≥24.5
Elongation (145,35min),%
≥340
≥330
SBR 1712 Specification (SH/T 1626-2005)
Item
Property
Test Method
A
B
C
Volatile matter% m/m
≤0.60
≤0.80
≤1.00
GB/T 6737-1997
Ash% (m/m)
≤0.50
GB/T 4498-1997
Organic acid %m/m
3.90-5.70
GB/T 8657-2000
Soap %m/m
≤0.50
Bound styrene% m/m
22.5-24.5
GB/T 8658-1998
Oil %m/m
25.3-29.3
24.3-30.3
SH/T 1718-2002
Mooney viscosity ML(1+4)100
44-54
43-55
42-56
GB/T 1232.1-2000
Compound ML(1+4)100
≤70
GB/T 1232.1-2000 ASTM IRB No.7
300%Modulus (145),MPa
25min
9.8-13.8
9.3-14.3
GB/T 8656-1998 ASTM IRB No.7
GB/T 528-1998 I
35min
12.1-16.1
11.6-16.6
50min
13.0-17.0
12.5-17.5
145,35min), MPa
Tensile strength
≥19.4
≥18.4
(145,35min), %
Elongation
≥380
≥370